M.I.O EPOXY AMINE adduct INTERMEDIATE – RANA 859 I
1-Good adhesion to properly pretreated
2-Can be used in systems for atmospheric or water
immersed exposure conditions.
3-Good abrasion resistance.
4-Good adhesion characteristics for subsequent coats.
5-Good resistance to industrial or chemical contaminated
atmospheric exposure conditions.
Volume solids: 62 ±2%
D.f.t: 50-70 microns
Specific gravity(mixed): 1.45 ± 0.05gr/cm3
Theoritical coverage: 12.4 m2 /lit (at 50 µ d.f.t)
Drying time at 25°c:
Touch dry: 5 hrs
Dry to handle: 16 hrs
Full cure: 4 days
Pot life: 3-4 hrs at 25 °c:
Mixing ratio(by volume):
Resin: refer to can label
Cure: refer to can label
Application methods: conventional spray or
Airless spray or roller
Recoat intervals* : 10°c 25°c 40°c
(mild condition) : Min: 15 hrs 6 hrs 3 hrs
**Max: NONE NONE NONE
**Maximum Recoat: Unlimited. Must have a clean, dry surface for top coating.”Loose” chalk or salts must be removed in . accordance with good painting practice. Drying time is temperature, humidity, and fi lm thickness dependent
Recommended thinner: RANA THINN 85
Recommended cleaner: RANA CLEAN 85
Shelf life: one year when stored indoors unopened
Original containers at 5 to 40°c (dry and cool place)
* : For recoating the surface should be free of dust ,grease and contamination.
Curing mechanism: by solvent release and reaction by
Curing agent and resin
Substrate: steel and primed steel
1-Zinc rich primed steel parts.
2-Galvanized steel sheets.
4-Shop primed steel.
This RANA CHEM’s product is a micaceous iron oxide epoxy
Polyamine adduct coating for industrial and marine use.
To obtain the maximum performance for which this product
is formulated,strict adherence to all application,instructions,
precautions,conditions and limitations is necessary.
The following equipment is listed as a guide and suitable
equipment from other manufactures may be used.
Adjustments of pressure and change of tip size may be
Needed to obtain the proper spray characteristics.
1-Airless spray:standard airless spray equipment having
a 28:1 or higher pump ratio and a fluid tip with a 0.457 to 0.660 mm
2-Conventional spray:industrial equipment with suitable
aircap having a fluid tip with a 2 – 2.2 mm orifice .
3 -Mixer:mixer must be powered by an air motor or an explosion
proof electric motor.
1-Handle with care.
2-Avoid inhalation of possible solvent vapours or
paint mist,as well as paint contact with skin and eyes.
3-Apply only in well ventilated areas and ensure that
adequate forced ventilation exists when paint applies is in
confined spaces or when the air is stagnant.
4-Always take precautions against the risks of fire
6-Harmful or fatal if swallowed,immediately seek medical
7-Use fresh air masks and explosion proof equipment.
1-Flush equipment with cleaner before use.
2-Stir resin to an even consistency with a power mixer.
3-Add cure to resin and continue stirring for 5 minutes.
Note: Since the pot life is limited and shortened by high
temperatures ,do not mix more material than will be used
in 3-4hours at 25 °c.
4-Thinning with RANA THINN 85 as needed for workability.
5-Stir during application to maintain uniformity of material
and apply a wet coat in even parallel passes after 20 minutes.
6-Clean all equipment with cleaner immediately after use
or at least at the end 0f each working day or shift .
Environmental temperature must be 10-40°c.
Surface temperature must be at least 3°c above dew point
to prevent condensation. At freezing temperature surface
must be free of ice and relative humidity below 80 %.
The surface must be clean and dry .All dirt grease and other
foreign materials should be removed .Old primed surface must
be smoothly wire brushed.