EPOXY SOLVENT FREE COAT RANA 932 T
EN.TDS
Product information
1- Excellent mechanical strength
2- Excellent resistance to abrasion
3- Excellent resistance to chemical material
4- Excellent resistance to oil
Physical data
Colour: customer request
Finish: flat to semi gloss
Flash point:
Resin: 24°c
Cure: 24°c
Volume solids: 88±2%
D.f.t: 200 – 5000 microns
Specific gravity(mixed): 1.45 ±0.05 gr/cm3
Theoretical coverage: 2.93 m2 /lit ( at 300µ d.f.t )
Drying time at 25°c:
Touch dry: 8 hrs
Full cure: 7 days
Component: 2
Pot life at 25°c: 60 minutes
Mixing ratio (by volume):
Resin: refer to label of can
Cure: refer to label of can
Application methods: Airless spray, hot airless
Recoat intervals* : 10°c 25°c 40°c
(mild condition) : Min: 16 hrs 8 hrs 4 hrs
**Max: NONE NONE NONE
**Maximum Recoat: Unlimited. Must have a clean, dry surface for top coating.”Loose” chalk or salts must be removed in . accordance with good painting practice. Drying time is temperature, humidity, and film thickness dependent
Recommended cleaner: RANA CLEAN 80
Shelf life: 6 months when stored indoors in unopened
Original containers at 5 to 40°c (cool and dry
Place).
Curing mechanism: reaction between components
Substrate: concrete, cement ,primed steel
* : For recoating the surface should be free of dust ,grease and contamination.
Typical uses
As a top coat on concrete or steel industrial
subjected to where chemical, solvents, mechanical
strength is required.
Application information
This RANA CHEM’s product is a two component poly amine
cured solvent free epoxy top coat.
To obtain the maximum performance for which this product
is formulated, strict adherence to all application, instructions,
precautions, conditions and limitations is necessary.
Application equipment
The following equipment is listed as a guide and suitable
equipment from other manufactures may be used.
adjustments of pressure and change of tip size may be
needed to obtain the proper spray characteristics.
1-Airless spray:standard airless spray equipment having
a 28:1 or higher pump ratio and a fluid tip with a 0.457 to 0.660 mm
orifice.
2- Hot airless
3 -Mixer: mixer must be powered by an air motor or an explosion
proof electric motor.
Caution
1-Handle with care.
2-Avoid inhalation of possible solvent vapours or
paint mist, as well as paint contact with skin and eyes.
3-Apply only in well ventilated areas and ensure that
adequate forced ventilation exists when applying paint
in confined spaces or when the air is stagnant.
4-Always take precautions against the risks of fire
and explosions.
5-Harmful or fatal if swallowed, immediately seek medical
assistance.
6-Use fresh air masks and explosion proof equipment.
Application procedures
1-Flush equipment with cleaner before use.
2-Stir resin to an even consistency with a power mixer.
3-Add cure to resin and continue stirring for 5 minutes.
Note: since the pot life is limited and shortened by high
temperatures ,do not mix more material than will be used
in 60 minutes at 25°c.
4-Stir during application to maintain uniformity of material
and apply a wet coat in even parallel passes and cross coat.
5-Clean all equipment with cleaner immediately after use.
Environmental condition
Environmental temperature must be 10-40°c.
Surface temperatures must be at least 3°c above dew point
to prevent condensation. At freezing temperatures surface
must be free of ice and relative humidity below 80 %.
Surface preparation
The surface must be clean, dry and free of grease,
mill scale, rust and dirt.