COAL TAR EPOXY – RANA 834 T
1-Ballast tank coating with outstanding water resistance.
2-Excellent corrosion resistance.
3-Good resistance against chemically polluted water.
4-Good abrasion resistance.
5-For tanklining,immersion or non-immersion service.
6-Superior application by airless and conventional spray.
7-Excellent adhesion to steel and concrete.
Colour: green, black , brown
Volume solids: 58±2%
D.F.T: 75 -100 microns
Specific gravity(mixed): 1.38 ± 0.05gr/cm3
Theoretical coverage: 8 m2 /lit (at 75 µ D.F.T)
Drying time at 25°c:
Touch dry: 4 hrs
Dry to handle: 10 hrs
Full cure: 7 days
Pot life: 8 hrs at 25 °c:
Mixing ratio(by volume):
Resin: refer to can lable
Cure: refer to can lable
Application methods: conventional spray or brush or
Airless spray or roller
Recoat intervals* : 10°c 25°c 40°c
(mild condition) : Min: 25 hrs 12 hrs 5 hrs
**Max: NONE NONE NONE
**Maximum Recoat: Unlimited. Must have a clean, dry surface for top coating.”Loose” chalk or salts must be removed in . accordance with good painting practice. Drying time is temperature, humidity, and fi lm thickness dependent
Recommended thinner: RANA THINN 80
Recommended cleaner: RANA CLEAN 80
Shelf life: 12 months when stored indoors in unopened
Original containers at 5 to 40°c (cool and dry
Curing mechanism: by solvent release and reaction by curing
Agent and resin
Substrate: steel, primed steel, concrete
*: For recoating the surface should be free of dust ,grease and contamination .
This RANA CHEM’s product is recommended for long time
corrosion protection of structural steel and concrete
in severe corrosive and immersed environments.
typical areas are steel buried in aggressive soil, pipelines
of steel and concrete, tanks containing fuel or lubrication
oil, drill water, drill mud, warm water or steel and concrete
in sewage treatment plants.
This product is a polyamide cured, coaltar epoxy
coating for non-immersion as well as immersion service
excellent corrosion and chemical resistance
and full film thickness in only one coat.
To obtain the maximum performance for which this product
is formulated strict adherence to all application instructions,
precautions, conditions and limitations is necessary.
The following equipment is listed as a guide and suitable
equipment from other manufactures may be used
Adjustments of pressure and change of tip size may be
needed to obtain the proper spray characteristics:
1-Airless spray: Standard airless spray equipment having
a 28:1 or higher pump ratio and a fluid tip with a 0.457 to 0.914 mm
2-Conventional spray:industrial equipment such with suitable
aircap having a fluid tip with a 1.8-2 mm orifice.
3-Mixer: use power mixer powered by an air motor or an
explosion proof electric motor.
1-Handle with care.
2-Before and during use ,observe all safety labels on
packaging and paint containers.
3-Harmful or fatal if swallowed ,immediately seek medical
4-Always take precautions against the fire and explosions.
5-Use with adequate ventilation.
6-Don’t empty into drains.
7-Take precautionary measures against static discharge.
1-Flush equipment with cleaner before use.
2-Stir resin to an even consistency with a power mixer.
3-Add cure to resin and continue stirring for 5 minutes.
Note: since the pot life is limited and shortened by high
temperatures ,do not mix more material than will be used
in 8 hours at 25 °c.
4- Thinning with RANA THINN80 as needed for workability .
5-Stir during application to maintain uniformity of material
and apply a wet coat in even parallel passes after 20 minutes.
6-Clean all equipment with cleaner immediately after use.
Environmental temperature must be 10-40°c.
Surface temperature must be at least 3°c above dew point
to prevent condensation. At freezing temperature surface
must be free of ice and relative humidity below 80 %.
The surface must be clean and dry . All dirt , grease ,
millscale and any other foreign material should be
removed.sand blasting to a standard of Sa 2.5 – Sa3 , SIS 05 5900 , ISO 8501-1.