GLASS FLAKE epoxy coating RANA 933 TG
1-High build glassflake epoxy coating.
2-Excellent oil resistance .
3-Excellent Salt and fresh water resistant.
4-Excellent chemical resistance against weak acids and alkalies.
5-Corrosion resistance in moderately to severely environment.
6- Solvent free epoxy coat.
Colour: customer request
Volume solids: 88±2 %
D.F.T: 200-5000 microns
Specific gravity(mixed): 1.48 ± 0.05gr/cm3
Theoretical coverage: 2.20 m2 /lit (at 400 µ D.F.T)
Drying time at 25°c:
Touch dry: 12hrs
Dry to handle: 24 hrs
Full cure: 7days
Pot life: 40 minute at 25 °c:
Mixing ratio(by volume):
Resin: refer to can label
Cure: refer to can label
Application methods: Airless spray or hot Airless spray
Recoat intervals* : 10°c 25°c 40°c
(mild condition) : Min: 16 hrs 9 hrs 5 hrs
**Max: NONE NONE NONE
**Maximum Recoat: Unlimited. Must have a clean, dry surface for top coating.”Loose” chalk or salts must be removed in . accordance with good painting practice. Drying time is temperature, humidity, and fi lm thickness dependent
Recommended cleaner: RANA CLEAN 80
Shelf life: 12 months when stored indoors in unopened
Original containers at 5 to 40°c (cool and dry
Curing mechanism: by solvent release and reaction by
Curing agent and resin
Substrate: steel , concrete
* : For recoating the surface should be free of dust ,grease and contamination.
As a high performance coating on steel and concrete
Structure in severe environments, including interior of
potable water tanks and oil tanks floors,
and other areas subject to marine weathering
and high humidity exposure .
This RANA CHEM’s product is a solvent free glassflake epoxy
for industrial and marine use.
To obtain the maximum performance for which this product
is formulated,strict adherence to all application,instructions,
precautions,conditions and limitations is necessary.
The following equipment is listed as a guide and suitable
equipment from other manufactures may be used.
adjustments of pressure and change of tip size may be
needed to obtain the proper spray characteristics.
1-Airless spray:standard airless spray equipment having
a 28:1 or higher pump ratio and a fluid tip with a 0.4 to 0.9 mm
2-Hot airless spray .
3 -Mixer: mixer must be powered by an air motor or an explosion
proof electric motor.
1-Handle with care.
2-Avoid inhalation of possible solvent vapours or
Paint mist,as well as paint contact with skin and eyes.
3-Apply only in well ventilated areas and ensure that
adequate forced ventilation exists when applying
paint in confined spaces or when the air is stagnant.
4-Always take precautions against the risks of fire
6-Harmful or fatal if swallowed, immediately seek medical
7-Use fresh air masks and explosion proof equipment.
1-Flush equipment with cleaner before use.
2-Stir resin to an even consistency with a power mixer.
3-Add cure to resin and continue stirring for 5 minutes.
Note: since the pot life is limited and shortened by high
temperatures ,do not mix more material than will be used
in 40 minute at 25°c.
4-Stir during application to maintain uniformity of material
and apply a wet coat in even parallel passes and cross coat.
5-Clean all equipment with cleaner immediately after use .
Environmental temperature must be 10-40°c.
Surface temperature must be at least 3°c above dew point
to prevent condensation. At freezing temperature surface
must be free of ice and relative humidity below 80 %.
The surface must be clean and dry .All dirt grease and other
foreign materials should be removed .Old primed surface
must be smoothly wire brushed. Sand blasting to standard Sa 2.5 – Sa3 ,
SIS 05 5900 , ISO 8501-1.