POLYURETHANE TOP COAT RANA 533 T
1-Provides excellent durability in industrial and
2-Suitable for environmental conditions where
other coatings can not be applied.
3-Excellent uv resistance
4-Resistant to water, impact and abrasion.
Colour: Customer request
Finish: Semi-Gloss/ Gloss
Volume solids: 50 ±2%
D.f.t: 50 – 60 microns
Specific gravity(mixed): 1.4.± 0.05gr/cm3
Theoretical coverage: 10 m2 /lit (at 50 µ d.f.t)
Drying time at 25°c:
touch dry: 3 hrs
dry to handle : 6 hrs
full cure: 7 days
Pot life: 6-8 hrs at 25°c:
Mixing ratio(by volume):
resin: Refer to can label
cure: Refer to can label
Application methods: Conventional spray or brush or
airless spray or roller
Recoat intervals* : 10°c 25°c 40°c
(mild condition) : Min: 16 hrs 8 hrs 4 hrs
**Max: NONE NONE NONE
**Maximum Recoat: Unlimited. Must have a clean, dry surface for top coating.”Loose” chalk or salts must be removed in . accordance with good painting practice. Drying time is temperature, humidity, and fi lm thickness dependent
Recommended thinner: RANA THINN 50
Recommended cleaner: RANA CLEAN 50
Shelf life: 12 months when stored indoors in unopened
Original containers at 5 to 40°c (cool and dry
Curing mechanism: By solvent release and reaction by
curing agent and resin
Substrate: Primed steel
*: For recoating the surface should be free of dust ,grease and contamination .
As a finishing coat for protection of structural steel
in severely corrosive environments where light-fastness
and gloss retention are required.
1-Steel structures in chemical and petrochemical industry,
power plants,tank farms,waste treatment plants.
2-Decks,boottops,top sides and superstructures of ships,
barges and work boats.
3-Piers,offshore platforms and related structures.
important:this product should not be stored above 30°c.
This RANA CHEM’s product is a polyurethane top coat
providing excellent protection for steel structures in
marine and industrial environments.
To obtain the maximum performance for which this product
is formulated,strict adherence to all application,instructions,
precautions,conditions and limitations is necessary.
The following equipment is listed as a guide and suitable
equipment from other manufactures may be used.
Adjustments of pressure and change of tip size may be
Needed to obtain the proper spray characteristics.
1-Airless spray:standard airless spray equipment having
A 28:1 or higher pump ratio and a fluid tip with a 0.33 to 0.38 mm
2-Conventional spray:industrial equipment
with suitable aircap having a fluid tip with A 1.4-1.6mm orifice .
3 -Mixer:mixer must be powered by an air motor or an explosion
proof electric motor.
4-Brush or roller.
1-Handle with care.
2-Avoid inhalation of possible solvent vapours or
paint mist, as well as paint contact with skin and eyes.
3-Apply only in well ventilated areas and ensure that
adequate forced ventilation exists when applying paint
in confined spaces or when the air is stagnant.
4-Always take precautions against the risks of fire
5-Harmful or fatal if swallowed, immediately seek medical
1-Flush equipment with cleaner before use.
2-Stir resin to an even consistency with a power mixer.
3-Add cure to resin and continue stirring for 5 minuts.
Note:since the pot life is limited and shortened by high
temperatures ,do not mix more material than will be used
in 8 hours at 25 °c .
4- Thinning with RANA THINN 50 as needed for workability .
5-Stir during application to maintain uniformity of material
and apply a wet coat in even parallel passes after 20 minutes.
6-Clean all equipment with cleaner immediately after use .
Environmental temperature must be 10-40°c
Surface temperature must be at least 3°c above dew point
to prevent condensation. At freezing temperature surface
must be free of ice and relative humidity below 80 %.
The surface must be clean and dry .all dirt, grease and other
foreign materials should be removed .old primed surface
must be smoothly wire brushed.